- Material
- PLA (Polylactic Acid)
- Recommended nozzle temperature
- 190–230°C
- Recommended bed temperature
- 35–45°C
- Recommended printing speed
- 250 mm/s
- Recommended drying settings
- 55°C for 8 hours
- Filament diameter
- 1.75 mm (0.03 mm)
- Density
- 1.22 g/cm³
- Vicat softening temperature
- 57°C
- Heat deflection temperature
- 56°C
- Melt index
- 32.2–4.5 g/10 min
- Tensile strength
- 33.4–42.3 MPa
- Breaking elongation rate
- 6.7–7.0% (0.5%)
- Bending modulus
- 2920–2490 MPa
- Bending strength
- 75.5–85.5 MPa
- Impact strength
- 24.0–24.0 kJ/m²
- Recommended humidity during printing
- 20% RH, sealed with desiccant